We describe the findings at six years in an ongoing prospective clinicoradiological and metal ion study in a cohort of 26 consecutive male patients with unilateral Birmingham Hip Resurfacing arthroplasties with one of two femoral head sizes (50 mm and 54 mm). Their mean age was 52.9 years (29 to 67). We have previously shown an early increase in the 24-hour urinary excretion of metal ions, reaching a peak at six months (cobalt) and one year (chromium) after operation. Subsequently there is a decreasing trend in excretion of both cobalt and chromium. The levels of cobalt and chromium in whole blood also show a significant increase at one year, followed by a decreasing trend until the sixth year.
If run-in wear is the only source of sustained metal release, then replacing the bearing with a non-MM bearing should not make a difference to metal release in patients and elevated levels should continue to persist even after such a revision. In order to verify this we studied metal release in patients who underwent revision of a MM bearing to a non-MM bearing after revision.
An earlier study (Clarke et al JBJS(Br) 2003) suggests that smaller bearings generate less wear. In that study bearings with different metallurgy and wear properties were grouped together, a potential confounding factor. The present study does not suffer from that error and our findings do not support the view that a larger bearing diameter leads to either an increase or decrease in metal ion generation.
Dislocation rates in large headed metal-on-metal resurfacings are extremely low. However, many patients are unsuitable for resurfacing and need a replacement. In such cases, it is attractive to transfer the large-headed metal-metal bearing advantage to replacement arthroplasty in order to reduce wear and dislocation rates. Does large diameter metal-metal total hip replacement really reduce the early dislocation rate?
Age at operation ranged from 37 to 83 years. Thirty patients were 55 years or under, eighty one were 56 – 65 years and ninety five were over 65 years. There were 122 females and 67 males. Posterior approach was used in all.
The extremely low failure rate in the medium term proves the suitability of resurfacing in young active patients. However, caution needs to be exercised until long term results are available.
There is sufficient evidence in this study to prove that metal ions do cross the placenta. There is therefore a continuing need for vigilance on the possible effects on the offspring born to patients with metal-metal devices.
Most friction studies are conducted in a bovine serum- carboxymethylcellulose (bs-cmc) medium. Following implantation however, the joint is bathed in blood which contains macromolecules and cells. The effect of these on friction is not fully understood. A progressive radiolucent line (fig 1) observed in some low clearance resurfacings raises the concern that increased friction may be affecting component fixation. The purpose of this investigation was to study the effect of clearance on friction for a given bearing diameter in the presence of blood as lubricant.
The results of this study suggest that reduced clearance bearings have the potential to generate higher friction when blood is the lubricant. this higher friction in the low clearance bearings may produce micromotion in the early postoperative period and hamper bony ingrowth resulting in impaired fixation with long-term implications for survival.
Old age, osteopaenia, alcohol abuse, and large cysts are risk factors for fractures. It has been suggested that performing a bilateral resurfacing puts the first side at risk of fracture from the force used in implanting the second resurfacing. Is this a true risk or a sampling error?
The low incidence of fractures (2/382, 0.5%) in this bilateral resurfacing series does not support the view that there is an increased risk of fracture from a bilateral procedure.
Bland-Altman analysis (Figure 1A) shows the limits of agreement between serum and WB are unacceptably wide (1.7 to -5.1 for chromium) suggesting poor agreement.
The dysplasia cup, which was devised as an adjunct to the Birmingham Hip Resurfacing system, has a hydroxyapatite-coated porous surface and two supplementary neutralisation screws to provide stable primary fixation, permit early weight-bearing, and allow incorporation of morcellised autograft without the need for structural bone grafting. A total of 110 consecutive dysplasia resurfacing arthroplasties in 103 patients (55 men and 48 women) performed between 1997 and 2000 was reviewed with a minimum follow-up of six years. The mean age at operation was 47.2 years (21 to 62) and 104 hips (94%) were Crowe grade II or III. During the mean follow-up of 7.8 years (6 to 9.6), three hips (2.7%) were converted to a total hip replacement at a mean of 3.9 years (2 months to 8.1 years), giving a cumulative survival of 95.2% at nine years (95% confidence interval 89 to 100). The revisions were due to a fracture of the femoral neck, a collapse of the femoral head and a deep infection. There was no aseptic loosening or osteolysis of the acetabular component associated with either of the revisions performed for failure of the femoral component. No patient is awaiting a revision. The median Oxford hip score in 98 patients with surviving hips at the final review was 13 and the 10th and the 90th percentiles were 12 and 23, respectively.
We report a retrospective review of the incidence of venous thromboembolism in 463 consecutive patients who underwent primary total hip arthroplasty (487 procedures). Treatment included both total hip replacement and hip resurfacing, and the patients were managed without anticoagulants. The thromboprophylaxis regimen included an antiplatelet agent, generally aspirin, hypotensive epidural anaesthesia, elastic compression stockings and early mobilisation. In 258 of these procedures (244 patients) performed in 2005 (cohort A) mechanical compression devices were not used, whereas in 229 (219 patients) performed during 2006 (cohort B) bilateral intermittent pneumatic calf compression was used. All operations were performed through a posterior mini-incision approach. Patients who required anticoagulation for pre-existing medical problems and those undergoing revision arthroplasty were excluded. Doppler ultrasonographic screening for deep-vein thrombosis was performed in all patients between the fourth and sixth post-operative days. All patients were reviewed at a follow-up clinic six to ten weeks after the operation. In addition, reponse to a questionnaire was obtained at the end of 12 weeks post-operatively. No symptomatic calf or above-knee deep-vein thrombosis or pulmonary embolism occurred. In 25 patients in cohort A (10.2%) and in ten patients in cohort B (4.6%) asymptomatic calf deep-vein thromboses were detected ultrasonographically. This difference was statistically significant (p = 0.03). The regimen followed by cohort B offers the prospect of a low incidence of venous thromboembolism without subjecting patients to the higher risk of bleeding associated with anticoagulant use.
The early designs of hip resurfacing implants suffered high rates of early failure, making it impossible to obtain valuable mid-term radiostereophotogrammetric (RSA) results. The metal-on-metal Birmingham Hip Resurfacing arthroplasty has shown promising mid-term results and we present here the first mid-term RSA analysis of a hip resurfacing implant. The analysis was performed in 19 hips at five years post-operatively. The mean acetabular component translation and rotation, and femoral component translation were compared with the previous RSA measurements at two and six months, and one and two years. There was no statistical significance (
Metal ions generated from joint replacements are a cause for concern. There is no consensus on the best surrogate measure of metal ion exposure. This study investigates whether serum and whole blood concentrations can be used interchangeably to report results of cobalt and chromium ion concentrations. Concentrations of serum and whole blood were analysed in 262 concurrent specimens using high resolution inductively-coupled plasma mass-spectrometry. The agreement was assessed with normalised scatterplots, mean difference and the Bland and Altman limits of agreement. The wide variability seen in the normalised scatterplots, in the Bland and Altman plots and the statistically significant mean differences between serum and whole blood concentrations suggest that they cannot be used interchangeably. A bias was demonstrated for both ions in the Bland-Altman plots. Regression analysis provided a possible conversion factor of 0.71 for cobalt and 0.48 for chromium. However, even when the correction factors were applied, the limits of agreement were greater than ±67% for cobalt and greater than ±85% for chromium, suggesting that serum and whole blood cannot be used interconvertibly. This suggests that serum metal concentrations are not useful as a surrogate measure of systemic metal ion exposure.