Abstract
Introduction: Increased wear is associated with aseptic loosening and late dislocations. Hard on hard bearings may reduce wear but still have topics of concern such as free metal ions in metal on metal bearings and the risk for fracture in ceramic articulations. Ceramic heads against conventional polyethylene is also used with the intention to reduce wear. But this effect has not been conclusively documented in the literature and is still discussed. 87 patients were operated consecutively by the same surgeon with the same surgical technique. All patients received a cemented all poly cup sterilized with irradiation in inert atmosphere and a cemented stem. Head size was 28 mm in all patients. 40 patients received cobalt-chrome heads and 47 patients aluminiumoxid heads. The patients were followed with RSA for 10 years and analysed for wear.
Results: Mean (SEM) wear for the group with cobalt chrome heads was 0.93 mm (0.13) and for the group with aluminiumoxide was 0.43 mm (0.08) (p = 0.001).
Discussion: We found significantly less wear with aluminumoxide heads compared to cobalt-chrome heads. The wear results in the cobalt-chrome group correlate well to wear values in the literature for conventional polyethylene. Although the polyethylene in this study is partly cross-linked (3Mrad) it is not clear whether these results can be extrapolated directly to the use of highly cross-linked PE. If longer follow-ups confirm the mechanical stability of highly cross-linked PE, ceramic heads might contribute additionally to the reduction of wear.
In conclusion we found significantly reduced wear for aluminumoxide heads compared to cobalt chrome heads which could be beneficial for young and active patients.
Correspondence should be addressed to BHS c/o BOA, at the Royal College of Surgeons, 35–43 Lincoln’s Inn Fields, London, WC2A 3PE, England.