Abstract
Since wear and loosening of the ultra-high-molecular-weight polyethylene cup are factors which limit the life of an arthroplasty we have attempted to identify factors associated with either low wear (0.02 mm/year or less) or high wear (0.2 mm/year or more). In a series of 1434 Charnley low-friction arthroplasties (1092 patients) 190 (13.2%) showed low wear while 149 (10.4%) showed high wear. We used chi-squared test to assess the significance of various factors.
The significant factors of the low-wear group were female gender (p = 0.042), rheumatoid arthritis (p = 0.014), Charnley grade C (p = 0.03) and varus position of the stem (p = 0.003). The use of acetabular cement pressurisation (p = 0.07) and medialisation of the cup (p = 0.07) approached significance.
In the high-wear group there was a predominance of men (p = 0.042) with osteoarthritis (p = 0.006) as the underlying hip pathology, and the stem in a valgus position (p = 0.023). Support of the cup by the rim of the acetabulum approached significance (p = 0.07). There was no statistical significance between the two groups for revision for aseptic loosening of the stem or fracture of the stem (p = 0.49). There was a highly significant difference (p < 0.0001) between the two groups for revision for wear and aseptic loosening of the cup, 5.3% compared with 39%.
Changes in the cup geometry are probably sufficient to explain the increasing incidence of loosening and revisions with the increasing depth of penetration of the cup. There is much to be gained from the use of a low-wearing ceramic-ultra-high-molecular-weight combination. Tissue reaction to the polyethylene particles cannot be the cause of aseptic loosening of the stem.