Abstract
The bone infection osteomyelitis (typically Staphylococcus aureus) requires a multistep treatment process including: surgical debridement, long-term systemic high-dose antibiotics, and often bone grafting. With antibiotic resistance becoming increasingly concerning, alternative approaches are urgently needed. Herein, we develop a one-step treatment for osteomyelitis that combines local, controlled release of non-antibiotic antibacterials (copper) within a proven regenerative scaffold. To maximise efficacy we utilised bioactive glass – an established material with immense osteogenic capacity – as a copper ion delivery reservoir. Copper ions have also been shown to stimulate angiogenesis and induce MSC differentiation down an osteogenic lineage. To eliminate grafting requirements, the copper-doped BG was incorporated into our previously developed collagen scaffolds to produce multifunctional antibacterial, osteogenic, and angiogenic scaffolds. Scaffolds were fabricated by freeze-drying a co-suspension of collagen and bioactive glass particles (+/− copper doping, referred to as CuBG and BG, respectively) at a range of different concentrations (0–300% w/w bioactive glass/collagen). Scaffolds demonstrated a 2.7-fold increase in compressive modulus (300% CuBG vs. 0%; p≤0.01), whilst maintaining >98% porosity. The 300% CuBG scaffolds showed significant antibacterial activity against Staphylococcus aureus (p≤0.001). In terms of osteogenesis, both 100% and 300% CuBG scaffolds increased cell-mediated calcium deposition on the scaffolds at day 14 and 28 (p≤0.05 and p≤0.001), as confirmed by alizarin red staining. 100% CuBG scaffolds significantly enhanced angiogenesis by increased tubule formation (p≤0.01) and VEGF protein production (p≤0.001) (all ≥n=3). In summary, this single-stage, off-the-shelf treatment for osteomyelitis shows potential to minimise bone grafting and antibiotic dependence, while reducing hospital stays and costs.