Abstract
The advantages of high viscosity Simplex AF cement (PMMA) compared to low viscosity Simplex P are the low porosity, the high fatigue strength, the lower polymerization time, and the lower maximum polymerization temperature. A prospective, randomized, double-blind clinical study was conducted to assess the in vivo effects of viscosity of bone cement on the micromotion of a polished tapered stem and UHMWP-cup (Exeter, Stryker-Howmedica). Roentgen Stereophotogrammetric Analysis (RSA-CMS, Medis, The Netherlands) was used to measure micromotion.
Twenty patients were included in a Simplex AF group (70 ± 4.3 years), and twenty patients were included in a Simplex P group (71 ± 7.3 years). No significant differences in body mass index and clinical hip scores were observed between the two studied groups.
There was no significant difference of the subsidence of both high and low viscosity cemented Exeter stems. The subsidence was according to the literature and showed that the viscosity of the bone cement did not influence the cement-implant bond of this polished tapered stem design.
The total migration of the cups and the migration along the medial-lateral axis were significantly larger for the Simplex AF cemented cups compared to the Simplex P cemented cups (p=0.037). This can be explained by the higher cement mantle thickness in acetabular Gruen zone 2 (p=0.003) and 3 (p=0.004) of the Simplex AF cemented cups.
We conclude from this study that the viscosity of the bone cement has no effect on the subsidence of polished tapered stems and that a high cement mantle thickness around an UHMWP-cup has a negative effect on fixation.