A leading problem with cementless hip replacement is thigh pain, probably due to some degree of loosening. This is most pronounced during activities such as stair climbing or getting up from a chair. Our study compares the immediate fixation of three stems in widespread clinical use, using a cadaver test simulation in which the femur was horizontal, and cyclic forces acted vertically downward on the prosthetic head with gradual increments of load. We implanted and tested 18 pairs of femurs, making analyses between stem types by right to left comparisons. We found no statistically significant differences in loosening between cementless AML and PCA prostheses, but cemented stems withstood greater loads than uncemented stems by a factor of five or more.

We have analysed the clinical results of a cementless hip replacement using a Moore stem with a smooth surface, and correlated these results with the radiological changes. Forty-two consecutive arthroplasties in 41 patients were studied prospectively and reviewed at a minimum of two and up to six years; 63% had a good clinical result, 18.5% a fair result, and 18.5% a poor result. Thigh pain on weight-bearing was the main problem and was due to loosening of the stem. We caution against the use of this implant in arthritic patients, in whom a good result can be obtained more predictably with cement fixation.

The purpose of this study was to establish if the Bateman prosthesis functions as a bipolar device moving primarily at the inner metal-on-polyethylene bearing as originally proposed, or as a unipolar hemiarthroplasty moving at the outer metal-on-cartilage surface as has recently been suggested. One hundred hips were examined at one year follow-up; 78 were examined again at two to four years. The replacement was performed for arthritis in 76 hips and for femoral neck fracture in 24. Movement was assessed both with and without weight-bearing. In 80% of the arthritis group the prosthesis functioned as a bipolar hip replacement with movement occurring primarily at the inner metal-on-polyethylene surface. By contrast, in 75% of the fracture group the prosthesis functioned largely as a unipolar device with movement occurring primarily at the outer metal-on-cartilage surface. In all cases examined serially the movement pattern was the same at two to four years as it has been at one year. Clearly, the action of the prosthesis depends on the condition of the acetabular cartilage.