There is widespread concern regarding the incidence of adverse soft-tissue reactions after metal-on-metal (MoM) hip replacement. Recent National Joint Registry data have shown clear differences in the rates of failure of different designs of hip resurfacing. Our aim was to update the failure rates related to metal debris for the Articular Surface Replacement (ASR). A total of 505 of these were implanted.

Kaplan-Meier analysis showed a failure rate of 25% at six years for the ASR resurfacing and of 48.8% for the ASR total hip replacement (THR). Of 257 patients with a minimum follow-up of two years, 67 (26.1%) had a serum cobalt concentration which was greater than 7 μg/l. Co-ordinate measuring machine analysis of revised components showed that all patients suffering adverse tissue reactions in the resurfacing group had abnormal wear of the bearing surfaces. Six THR patients had relatively low rates of articular wear, but were found to have considerable damage at the trunion-taper interface. Our results suggest that wear at the modular junction is an important factor in the development of adverse tissue reactions after implantation of a large-diameter MoM THR.

Increased femoral head size may reduce dislocation rates following total hip replacement. The National Joint Registry for England and Wales has highlighted a statistically significant increase in the use of femoral heads ≥ 36 mm in diameter from 5% in 2005 to 26% in 2009, together with an increase in the use of the posterior approach. The aim of this study was to determine whether rates of dislocation have fallen over the same period. National data for England for 247 546 procedures were analysed in order to determine trends in the rate of dislocation at three, six, 12 and 18 months after operation during this time. The 18-month revision rates were also examined.

Between 2005 and 2009 there were significant decreases in cumulative dislocations at three months (1.12% to 0.86%), six months (1.25% to 0.96%) and 12 months (1.42% to 1.11%) (all p < 0.001), and at 18 months (1.56% to 1.31%) for the period 2005 to 2008 (p < 0.001). The 18-month revision rates did not significantly change during the study period (1.26% to 1.39%, odds ratio 1.10 (95% confidence interval 0.98 to 1.24), p = 0.118). There was no evidence of changes in the coding of dislocations during this time.

These data have revealed a significant reduction in dislocations associated with the use of large femoral head sizes, with no change in the 18-month revision rate.

Diagnostic and operative codes are routinely collected for every patient admitted to hospital in the English NHS. Data on post-operative complications following foot and ankle surgery have not previously been available in large numbers. Data on symptomatic venous thromboembolism events and mortality within 90 days were extracted for patients undergoing fixation of an ankle fracture, first metatarsal osteotomy, hindfoot fusions and total ankle replacement over a period of 42 months. For ankle fracture surgery (45 949 patients), the rates of deep-vein thrombosis (DVT), pulmonary embolism and mortality were 0.12%, 0.17% and 0.37%, respectively. For first metatarsal osteotomy (33 626 patients), DVT, pulmonary embolism and mortality rates were 0.01%, 0.02% and 0.04%, and for hindfoot fusions (7033 patients) the rates were 0.03%, 0.11% and 0.11%, respectively. The rate of pulmonary embolism in 1633 total ankle replacement patients was 0.06%, and there were no recorded DVTs and no deaths. Statistical analysis could only identify risk factors for venous thromboembolic events of increasing age and multiple comorbidities following fracture surgery.

Venous thromboembolism following foot and ankle surgery is extremely rare, but this subset of fracture patients is at a higher risk. However, there is no evidence that thromboprophylaxis reduces this risk, and these national data suggest that prophylaxis is not required in most of these patients.

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear.

We present the early clinical and radiological results of Articular Surface Replacement (ASR) resurfacings in 214 hips (192 patients) with a mean follow-up of 43 months (30 to 57). The mean age of the patients was 56 years (28 to 74) and 85 hips (40%) were in 78 women.

The mean Harris hip score improved from 52 (11 to 81) to 95 (27 to 100) at two years and the mean University of California, Los Angeles activity score from 3.9 (1 to 10) to 7.4 (2 to 10) in the same period. Narrowing of the neck (to a maximum of 9%) was noted in 124 of 209 hips (60%). There were 12 revisions (5.6%) involving four (1.9%) early fractures of the femoral neck and two (0.9%) episodes of collapse of the femoral head secondary to avascular necrosis. Six patients (2.8%) had failure related to metal wear debris. The overall survival for our series was 93% (95% confidence interval 80 to 98) and 89% (95% confidence interval 82 to 96) for hips with acetabular components smaller than 56 mm in diameter.

The ASR implant has a lower diametrical clearance and a subhemispherical acetabular component when compared with other more frequently implanted metal-on-metal hip resurfacings. These changes may contribute to the higher failure rate than in other series, compared with other designs. Given our poor results with the small components we are no longer implanting the smaller size.

Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear.

Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement.

The National Institute for Clinical Excellence (NICE) produces recommendations on appropriate treatment within the National Health Service (NHS) in England and Wales. The NICE guidelines on prophylaxis for venous thromboembolism in orthopaedic surgery recommend that all patients be offered a low molecular weight heparin (LMWH). The linked hospital episode statistics of 219 602 patients were examined to determine the rates of complications following lower limb arthroplasty for the 12-month periods prior to and following the publication of these guidelines. These were compared with data from the National Joint Registry (England and Wales) regarding the use of LMWH during the same periods. There was a significant increase in the reported use of LMWH (59.5% to 67.6%, p < 0.001) following the publication of the guidelines. However, the 90-day venous thromboembolism events actually increased slightly following total hip replacement (THR, 1.69% to 1.84%, p = 0.06) and remained unchanged following total knee replacement (TKR, 1.99% to 2.04%). Return to theatre in the first 30 days for infection did not show significant changes. There was an increase in the number of patients diagnosed with thrombocytopenia, which was significant following THR (0.11% to 0.16%, p = 0.04). The recommendations from NICE are based on predicted reductions in venous thromboembolism events, reducing morbidity, mortality and costs to the NHS.

The early results in orthopaedic patients do not support these predictions, but do show an increase in complications.

Increased concentrations of metal ions after metal-on-metal resurfacing arthroplasty of the hip remain a concern. Although there has been no proven link to long-term health problems or early prosthetic failure, variables associated with high metal ion concentrations should be identified and, if possible, corrected. Our study provides data on metal ion levels from a series of 76 consecutive patients (76 hips) after resurfacing arthroplasty with the Articular Surface Replacement. Chromium and cobalt ion concentrations in the whole blood of patients with smaller (≤ 51 mm) femoral components were significantly higher than in those with the larger (≥ 53 mm) components (p < 0.01). Ion concentrations in the former group were significantly related to the inclination (p = 0.01) and anteversion (p = 0.01) of the acetabular component. The same relationships were not significant in the patients with larger femoral components (p = 0.61 and p = 0.49, respectively). Accurate positioning of the acetabular component intra-operatively is essential in order to reduce the concentration of metal ions in the blood after hip resurfacing arthroplasty with the Articular Surface Replacement implant.