Pitting damage on implants has been reported and attributed to use of electrocautery. This study aimed to distinguish how different TKA bearing surfaces are susceptible to this type of damage and whether surgeons were aware that this damage can occur. A survey was sent to Hip and Knee Society members to determine what percentage of adult reconstructive surgeons use electrocautery after implantation of components. Three bearing surfaces for primary TKA were selected: CoCr, Oxinium, and zirconium nitride (ZrN) to be damaged by electrocautery with a monopolar (MP, Bovie) and bipolar (BP, Aquamantys) electrocautery with three different energy settings. A comparison of surface damage and backscatter elemental analysis using SEM was performed. Average roughness (Ra), maximal peak-to-valley height (Rz,), kurtosis (Rk), and skewness (Rsk) measurements were collected using a profilometer (DektakXT, Bruker, Tucson, AZ) with a 2.5µm radius stylus to assess an area of 3.8mm by 3.2mm in the central portion of the area for each MP and BP energy setting used to impart damage to the bearing surfaces. A similar undamaged area for each bearing surface was also measured for roughness parameter comparison.Introduction
Methods
This study aimed to determine if macrophages can attach and directly affect the oxide layers of 316L stainless steel, titanium alloy (Ti6Al4V), and cobalt-chromium-molybdenum alloy (CoCrMo) by releasing components of these alloys. Murine peritoneal macrophages were cultured and placed on stainless steel, CoCrMo, and Ti6Al4V discs into a 96-well plate. Cells were activated with interferon gamma and lipopolysaccharide. Macrophages on stainless steel discs produced significantly more nitric oxide (NO) compared to their control counterparts after eight to ten days and remained elevated for the duration of the experiment.Aims
Methods