During the past decades, novel materials have been developed to improve osseointegration of implants. Recently has been demonstrated that by using nanosized hydroxyapatite (HA) coatings, since it combines nanoroughness and bone-like chemistry in a synergistic effect, it promotes better osseointegration when compared to uncoated metal implants. In a further step, due to the known bactericidal properties of fluor, the aim of this study is to evaluate the biofilm development on fluorohydroxyapatite (FHA) compared to HA.

Coatings were grown on stainless steel substrates by Pulsed Laser Deposition (PLD) technique using fluorohydroxyapatite targets of marine origin. A comprehensive physicochemical characterization of the coatings was performed using SEM, EDS, XPS and XRD. Biological in vitro tests using the pre-osteoblastic cell line (MC3T3-E1) demonstrated the non-cytotoxicity of FHA coatings, the healthy cell proliferation and their osteogenic activity.

The S. aureus 15981 (Valle et al.) and S. epidermidis ATCC 35984 strains adherence study was performed introducing each probe in a well of 96-well plate with 200 µl containing 106 colony forming units (CFU/mL) intryptic soy broth supplemented with 1% glucose and was incubated at 37°C 5% CO2 for 24 hours. After incubation, the medium was removed and three washes with 0.9% NaCl sterile saline were performed. The biofilm was disrupted by sonication at 50–60 Hz for 5 min. The CFU/cm2 was estimated by drop plate method. All of the experiments were performed in triplicate.

Statistical analysis was performed by non-parametric unilateral Wilcoxon”s test with a level of statistical significance of 0.05.

The results showed a significant (p=0.02475) 2.4-fold reduction in S. epidermidis biofilm formation on FHA (logUFC/cm2 = 6.87) compared to HA (logUFC/cm2 = 7.25); and also a significant (p=0.042) 3.7-fold reduction in S. aureus 15981 biofilm formation.

In conclusion, according our results FHA is a promising biomaterial that promotes osseointegration and decreases the staphylococcal biofilm that could avoid PJI. Further studies will be necessary.

Introduction and objectives

High-energy pelvic fractures are life-threatening injuries. Approximately 15% to 30% of patients with high-energy pelvic injuries are hemodynamic unstable, hemorrhagic shock remains the main cause of death in patients with pelvic fractures, with an overall mortality rate from 6% to 35%. The correlation between fracture pattern and mortality in polytrauma with pelvic fracture has been previously investigated. However, the purpose of our investigation was to evaluate the relationship of hemodynamic instability with the pelvic fracture pattern according to different classifications.

Introduction and objectives

Intramedullary nailing is indicated to stabilization of tibia shaft fractures. Intramedullary nailing through an infra-patellar incision is commonly the technique of choice. While intramedullary nailing of simple diaphyseal fracture patterns is relatively easy, proximal tibia fractures, extremely comminuted/segmental tibia fractures, politrauma with multiple fractures in both extremities and reconstruction of bone loss segment with stiffness of the knee joint can be very challenging to treat.

A novel technique for intramedullary tibia nailing through the patella-femoral joint is described. This technique allow extension tibia during intervention time and it supplies easier reduction of the pattern of fracture above. The purpose of our investigation was to evaluate the use of this new technique in described above pattern fracture and patient situation; because we have thought that new technique can perform better outcomes in this situations.