A disturbing prevalence of painful inflammatory reactions has been reported in metal-on-metal (MoM) hip resurfacing arthroplasty. A contributing factor is localized loading of the acetabular shell leading to “edge wear” which is often seen after precise measurement of the bearing surfaces of retrieved components. Factors contributing to edge wear include adverse cup orientation leading to proximity (<10 mm) of the hip reaction force to the edge of the acetabular component. As this phenomenon is a function of implant positioning and patient posture, this study was performed to investigate the occurrence of edge loading during different functional activities as a function of cup inclination and version. We developed a computer model of the hip joint through reconstruction of CT scans of a proto-typical pelvis and femur and virtually implanting a hip resurfacing prosthesis in an ideal position. Using this model, we examined the relationship between the resultant hip force vector and the edge of the acetabular shell during walking, stair ascent and descent, and getting in and out of a chair. Load data was derived from 5 THR patients implanted with instrumented hip prostheses (Bergmann et al). We calculated the distance from the edge of the shell to the point of intersection of the load vector and the bearing surface for cup orientations ranging from 40 to 70 degrees of inclination, and 0 to 40 degrees of anteversion.Introduction:
Methods:
Recent retrieval studies and registry reports have demonstrated an alarming incidence of early failure of metal-on-metal THR. This appears to be due to fretting and corrosion at the taper junction (trunnion) between the neck and large diameter heads in metal-on-metal hip implants. It has been proposed that designs with lower bearing clearances and greater cup flexibility deform during implantation leading to increased frictional torque and micromotion at the head-neck taper junction. Small movements at the trunnion may suggest elastic deformation, but large movements may suggest slippage at the friction interface. This study was conducted using retrieved metal-on-metal components to test the hypotheses that: 1. Cup deformation through localized compression leads to increased bearing torque, and 2. Increased torques generated in large head metal-on-metal bearings cause motion of the head-neck taper junction. Nine metal-on-metal hip implants were received from a national joint retrieval service and tested in a mechanical testing machine. The components were of three different designs (ASR, BHR, and Durom) and ranged in diameter from 42–54 mm. A custom jig was constructed to generate controlled radial compression at opposite points on the rim of an acetabular component. The jig was positioned inverted to the normal anatomical position and was angled to simulate the anatomical orientation of the cup (35° inclination, 10° anteversion). With the exception of an initial compression load of 100N, the cups were compressed at 200N intervals to a maximum of 2000N. Three trials at each cup compression load were performed. The torque developed about the trunnion axis was measured as the head articulated through a motion arc of 60° and the friction factor was calculated. Head–neck micromotion was continuously monitored using a non-displacement inductive transducer. Changes in micromotion from the 100N compression load were calculated.Introduction
Materials and Methods
A disturbing prevalence of short-term failures of metal-on-metal (MoM) hip resurfacings has been reported by joint registries. These cases have been primarily due to painful inflammatory reactions and, in extreme cases, formation of pseudotumors within periarticular soft-tissues. The likely cause is localized loading of the acetabular shell leading to “edge wear” which is often seen after precise measurement of the bearing surfaces of retrieved components. Factors contributing to edge wear of metal-on-metal arthroplasties are thought to include adverse cup orientation, patient posture, and the direction of hip loading. The purpose of this study was to investigate the role of different functional activities in edge loading of hip resurfacing prostheses as a function of cup inclination and version. We developed a computer model of the hip joint through reconstruction of CT scans of a proto-typical pelvis and femur and virtually implanting a hip resurfacing prosthesis in an ideal position. Using this model, we examined the relationship between the resultant hip force vector and the edge of the acetabular shell during walking, stair ascent and descent, and getting in and out of a chair. Load data was derived from 5 THR patients implanted with instrumented hip prostheses (Bergmann et al). We calculated the distance from the edge of the shell to the point of intersection of the load vector and the bearing surface for cup orientations ranging from 40 to 70 degrees of inclination, and 0 to 40 degrees of anteversion.Introduction
Methods
Edge loading is a common wear mechanism in Metal-on-Metal (MOM) hip resurfacing and is associated with higher wear rates and the incidence of pseudotumour. The purpose of this study was to develop a method to investigate the contributions of patient, surgical and implant design variables on the risk of edge loading. We created a mathematical model to calculate the distance from the head-cup contact patch to the rim of the cup and used this to investigate the effect of component position, specific design features and patient activity on the risk of edge loading. We then used this method to calculate the contact patch to rim distance (CPRD) for 160 patients having undergone revision of their MOM hip resurfacing in order to identify any possible associations.Introduction
Method
It has been speculated that impact deformation of thin 1-piece cups used for modern metal-on-metal hip replacement may contribute to early failure. The purpose of this study was to reproduce typical impact deformation and quantify the effect of this on the frictional torque generated at the hip. We tested nine hip couples of three designs (the ASR, BHR and Durom) and three sizes (42mm, 46mm and 50mm). A custom compression device was designed to replicate the in vivo forces and impact deformation of 1-piece metal cups reported in the literature. Each cup was mounted in the device, which itself was mounted on a mechanical testing machine. The cups were compressed with incremental loads up to a maximum of 2000N. At each increment we measured cup deformation, and then the head component was seated into the cup. The hip was lubricated and the head component rotated 60 degrees axially within the cup and the axial torque was measured.Introduction
Methods