In the elderly population, chronic rotator cuff tears are often associated with high re-rupture rates after surgical tendon refixation. Implant materials, especially in combination with additives are supposed to positively influence healing outcome. Furthermore, adequate mechanical properties are crucial. In order to realize degradable implants with high specific surface area, polycaprolactone (PCL) was chosen as basic material and processed by electrospinning to achieve a high surface area for growth factor implementation and subsequent cell attachment. PCL (Mn approx. 80,000 g/mol) was used to generate fibre mats by electrospinning (relative collector velocity 8 m/s; flow rate of 4 ml/h). Mechanical analysis was performed according to EN ISO 527–2:2012 with test specimen 1BA (5 mm in diameter). Maximum force at failure (Fmax) as well as stiffness were evaluated. For preclinical in vivo testing, a coating with CS-g-PCL was performed to increase cellular adhesion and biological integration. Native and TGF-ß3 loaded mats were examined in a chronic rat tendon defect model with dissection of the M. infraspinatus, four week latency and following refixation at the humerus with different PCL-fibre mats (approval Nr. 33.12–42502–04–15/2015). After 8 weeks, rats were finalized and tendon-bone insertions were analyzed biomechanically and via histological methods.Introduction and Objective
Materials and Methods