Regeneration of cartilage injuries is greatly limited. Therefore, cartilage injuries are often the starting point for later osteoarthritis. In the past, various bioactive glass (BG) scaffolds have been developed to promote bone healing. Due to the fact that they induce the deposition of hydroxyapatite (HA) -the main component of bone matrix, these BG types are not suitable for chondrogenesis. Hence, a novel BG (Car12N) lacking HA formation, was established. Since BG are generally brittle the combination with polymers is helpful to achieve suitable biomechanic stability. The aim of this interdisciplinary project was to investigate the effects of biodegradable polymer Poly(D,L-lactide-co-glycolide) (PLLA) infiltration into a Car12N scaffold for cartilage tissue engineering. BG scaffolds were infiltrated with PLLA using phase separation within a solvent. Pure BG Car12N scaffolds served as control. To assess whether the polymer was homogeneously distributed the polymer to glass ratio and pore contents in the upper, middle and lower third of the scaffolds were examined by light microscopy. For a more precise characterization of the scaffold topology, the glass strut length, the glass strut diameter and the pore circumference were also measured. Leaching tests in 0.1M HCl solution over 8 days were used to allow a gel layer formation on the scaffolds surface. Non-leached and leached scaffolds were subjected to strength testing. Cytotoxicity of the scaffolds with and without polymer was tested according to standards. Scaffolds were colonized with 27.777.8 per cm3 primary porcine articular chondrocytes (pACs) or primary human mesenchymal stromal cells (hMSCs), respectively. After cultivation for up to 35 days, the vitality, quantitative DNA and sulfated glycosaminoglycan (sGAG) contents per scaffold were determined.Introduction and Objective
Materials and Methods
Cartilage injuries often represent irreversible tissue damage because cartilage has only a low ability to regenerate. Thus, cartilage loss results in permanent damage, which can become the starting point for osteoarthritis. In the past, bioactive glass scaffolds have been developed for bone replacement and some of these variants have also been colonized with chondrocytes. However, the hydroxylapaptite phase that is usually formed in bioglass scaffolds is not very suitable for cartilage formation (chondrogenesis). This interdisciplinary project was undertaken to develop a novel slowly degrading bioactive glass scaffold tailored for cartilage repair by resembling the native extracellular cartilage matrix (ECM) in structure and surface properties. When colonized with articular chondrocytes, the composition and topology of the scaffolds should support cell adherence, proliferation and ECM synthesis as a prerequisite for chondrogenesis in the scaffold. To study cell growth in the scaffold, the scaffolds were colonized with human mesenchymal stromal cells (hMSCs) and primary porcine articular chondrocytes (pACs) (27,777.8 cells per mm3) for 7 – 35 d in a rotatory device. Cell survival in the scaffold was determined by vitality assay. Scanning electron microscopy (SEM) visualized cell ultramorphology and direct interaction of hMSCs and pACs with the bioglass surface. Cell proliferation was detected by CyQuant assay. Subsequently, the production of sulphated glycosaminoglycans (sGAGs) typical for chondrogenic differentiation was depicted by Alcian blue staining and quantified by dimethylmethylene blue assay assay. Quantitative real-time polymerase chain reaction (QPCR) revealed gene expression of cartilage-specific aggrecan, Sox9, collagen type II and dedifferentiation-associated collagen type I. To demonstrate the ECM-protein synthesis of the cells, the production of collagen type II and type I was determined by immunolabelling. The bioactive glass scaffold remained stable over the whole observation time and allowed the survival of hMSCs and pACs for 35 days in culture. The SEM analyses revealed an intimate cell-biomaterial interaction for both cell types showing cell spreading, formation of numerous filopodia and ECM deposition. Both cell types revealed initial proliferation, decreasing after 14 days and becoming elevated again after 21 days. hMSCs formed cell clusters, whereas pACs showed an even distribution. Both cell types filled more and more the pores of the scaffold. The relative gene expression of cartilage-specific markers could be proven for hMSCs and pACs. Cell associated sGAGs deposition could be demonstrated by Alcian blue staining and sGAGs were elevated in the beginning and end of the culturing period. While the production of collagen type II could be observed with both cell types, the synthesis of aggrecan could not be detected in scaffolds seeded with hMSCs. hMSCs and pACs adhered, spread and survived on the novel bioactive glass scaffolds and exhibited a chondrocytic phenotype.
