In 2010, a widely used metal-on-metal hip implant was voluntarily recalled from the market by the manufacturer. Our lab performed detailed retrieval analysis of 548 of the explanted devices and 165 periprosthetic tissue specimens. We reported a high degree of variability in the multiple measurements that we performed on the components, including volumetric wear. Other studies using semi-quantitative tissue grading methods to describe the histology of the periprosthetic tissues from metal-on-metal hips have looked for relationships between component wear and histological features. Grammatopoulos et al found higher ALVAL scores in 45 hip resurfacing patients with pseudotumors compared to 11 without pseudotumors and a moderately positive correlation between wear and the histological rankings for tissue necrosis and lymphocytic response. We examined correlations between the component wear measurements from retrieval analysis and the tissue features in this large group of one metal-on-metal hip design. Tissues were processed routinely into paraffin sections, stained with H&E and characterized with light microscopic semi-quantitative scores for ALVAL features and for the number of macrophages and lymphocytes, extent of metal debris and the estimated percentage of necrosis per slide. Spearman correlation analysis was conducted to evaluate any correlations between retrieval wear measurements and histological findings.Introduction
Materials and Methods
We describe three prostheses with cemented titanium-alloy stems and Al2O3 ceramic femoral heads which had to be revised after a mean period of implantation of 78 months. In each case, the neck of the prosthesis had been so severely worn that the profile was elliptical rather than circular. There was severe metallosis of the periprosthetic tissues. Metal particles isolated from the tissues were approximately one nanometre in size and the ratios of titanium, aluminium and vanadium in the particles were the same as in the original alloy. Histologically, the high concentration of metal particles masked the presence of high-density polyethylene (HDP) debris, but again particles about one nanometre in size were isolated from the tissues. The severe necrobiosis and necrosis noted were consistent with other reports of the presence of extensive wear particles in periprosthetic tissues. Wear is presumed to have occurred as a result of mismatch between the shape or size of the taper cone and the femoral head, or to changes in the geometry of loading due to migration of the cup. To facilitate early intervention, patients with this design of prosthesis should be monitored radiologically.