The aim of this study was test the amount of corrosion occurring at the (Ti) /cobalt chrome (CoCr) interface comparing this with Ti and Ti interfaces. This was compared with retrieved metal work visualised under a scanning electron microscope (SEM). The interface of interest is the interface between rod and the screw. We investigated corrosion seen at that interface with a CoCr rod coupled to a Ti screw versus a Ti rod coupled to a Ti screw (6 screws were used) Implants were loaded according to the ASTM F2193 – 02 Standard Specifications and Test Methods for Components Used in the Surgical Fixation of the Spinal Skeletal System. Pitting potentials were monitored using cyclic potentiodynamic polarization tests (ASTM F2129 – 08 Standard Test Method for Conducting Cyclic Potentiodynamic Polarisation Measurements) to determine corrosion susceptibility. Retrieved implants were visualised under (SEM) to confirm corrosion.Aim:
Methods:
Due to absence of fusion in guided-growth devices for EOS (growing rods, Shilla, LSZ) movement of the rods against their attachment is possible resulting in wear debris formation. It is important to understand the wear resistance of materials used in these devices under appropriate conditions. The aim of our work was to investigate wear resistance of titanium alloy Ti-6Al-4V and superelastic Nitinol. Nitinol has been used recently for correcting scoliosis and may provide a better and more gradual correction than other materials.Introduction:
Aim: