Impingement of total hip replacements (THRs) can cause rim damage of polyethylene liners, and lead to dislocation and/or mechanical failure of liner locking mechanisms[1]. A geometric model of a THR in situ was previously developed to predict impingement for different component orientations and joint motions of activities[2]. However, the consequence of any predicted impingement is unknown. This study aimed to develop an in-vitromethod to investigate the effects of different impingement scenarios. A ProSim electro-mechanical single-station hip simulator (Simulation Solutions) was used, and the 32mm diameter metal-on-polyethylene THRs (DePuy Synthes) were assessed. The THR was mounted in an inverted orientation, and the input (motion and loading) applied simulated a patient stooping over to pick an object from the floor[3]. The impingement severity was varied by continuing motion past the point of impingement by 2.5° or 5°, and compressive load applied in the medial-lateral direction was varied from 100N to 200N. Each test condition was applied for 40,000 cycles (n=3). Rim penetration was assessed using a CMM and component separation was measured during the tests.Abstract
Objectives
Method
Many factors contribute to the occurrence of edge-loading conditions in hip replacement; soft tissue tension, surgical position, patient biomechanical variations and type of activities, hip design, etc. The aim of this study was to determine the effect of different levels of rotational and translational surgical positioning of hip replacement bearings on the occurrence and severity of edge-loading and the resultant wear rates. The Leeds II Hip-Joint Simulator and 36mm diameter alumina matrix composite ceramic bearings (BIOLOX delta, DePuy Synthes, UK) were used in this study. Different levels of mismatch between the reconstructed rotational centres of the head and the cup were considered (2, 3 and 4mm) in the medial-lateral axis. Two cup inclination angles were investigated; an equivalent to 45 and 65 degrees in-vivo, thus six conditions (n=6 for each condition) were studied in total with three million cycles completed for each condition. The wear of the ceramic-on-ceramic bearings were determined using a microbalance (Mettler Toledo, XP205, UK) and the dynamic microseparation displacement was measured using a Liner Variable Differential Transformer.Background
Method
Edge loading due to dynamic separation can occur due to variations in component positioning such as a steep cup inclination angle (rotational) or mismatch between the centres of rotation of the head and the cup (translational). The aim of this study was to determine the effect of variations in rotational and translational positioning of the cup on the magnitude of dynamic separation, wear and deformation of metal-on-polyethylene bearings. Eighteen 36mm diameter metal-on-polyethylene hip replacements were tested on an electromechanical hip simulator. Standard gait with concentric head and cup centres were applied for cups inclined at 45° (n=3) and 65° (n=3) for two million cycles. A further two tests with translational mismatch of 4mm applied between the head and cup bearing centres for cups inclined at 45° (n=6) and 65° (n=6) were run for three million cycles. Wear was determined using a microbalance and deformation by geometric analysis. Confidence intervals of 95% were calculated for mean values, and t-tests and ANOVA were used for statistical analysis (p<0.05). Under 4mm mismatch conditions, a steeper cup inclination angle of 65° resulted in larger dynamic separation (2.1±0.5mm) compared with cups inclined at 45° (0.9±0.2mm). This resulted in larger penetration at the rim under 65° (0.28±0.04mm) compared to 45° (0.10±0.09mm) cup inclination conditions (p<0.01). Wear rates under standard concentric conditions were 12.8±3.8 mm3/million cycles and 15.4±5.0 mm3/million cycles for cups inclined at 45° and 65° respectively. Higher wear rates were observed under 4mm of translational mismatch compared with standard concentric conditions at 45° (21.5±5.5 mm3/million cycles, p<0.01) and 65° (23.0±5.7 mm3/million cycles, p<0.01) cup inclination. Edge loading under dynamic separation conditions due to translational mismatch resulted in increased wear and deformation of the polyethylene liner. Minimising the occurrence and severity of edge loading through optimal component positioning may reduce the clinical failure rates of polyethylene.
Edge loading due to dynamic separation can occur due to variations in component positioning such as a steep cup inclination angle (rotational) or mismatch between the centres of rotation of the head and the cup (translational). The aim of this study was to determine the effect of variations in rotational and translational positioning of the cup on the magnitude of dynamic separation, wear and deformation of metal-on-polyethylene bearings. Eighteen 36mm diameter metal-on-polyethylene hip replacements were tested on an electromechanical hip simulator. Standard gait with concentric head and cup centres were applied for cups inclined at 45° (n=3) and 65° (n=3) for two million cycles. A further two tests with translational mismatch of 4mm applied between the head and cup bearing centres for cups inclined at 45° (n=6) and 65° (n=6) were run for three million cycles. Wear was determined using a microbalance and deformation by geometric analysis. Confidence intervals of 95% were calculated for mean values, and t-tests and ANOVA were used for statistical analysis (p<0.05). Under 4mm mismatch conditions, a steeper cup inclination angle of 65° resulted in larger dynamic separation (2.1±0.5mm) compared with cups inclined at 45° (0.9±0.2mm). This resulted in larger penetration at the rim under 65° (0.28±0.04mm) compared to 45° (0.10±0.05mm) cup inclination conditions (p<0.01). Wear rates under standard concentric conditions were 12.8±3.8 mm3/million cycles and 15.4±5.0 mm3/million cycles for cups inclined at 45° and 65° respectively. Higher wear rates were observed under 4mm of translational mismatch compared with standard concentric conditions at 45° (21.5±5.5 mm3/million cycles, p<0.01) and 65° (23.0±5.7 mm3/million cycles, p<0.01) cup inclination. Edge loading under dynamic separation conditions due to translational mismatch resulted in increased wear and deformation of the polyethylene liner. Minimising the occurrence and severity of edge loading through optimal component positioning may reduce the clinical failure rates of polyethylene.
Wear particles produced by alumina ceramic-on-ceramic (CoC) bearings cause a minimal immunological response with low cytotoxicity and inflammatory potential1, 2. However, more comprehensive immunological studies are yet to be completed for the composite CoC (zirconia-toughened, platelet reinforced alumina) hip replacements due to difficulties in isolating the very low volume of clinically relevant wear debris generated by such materials Composite ceramic particles (commercial BIOLOX® delta powder) were obtained from CeramTec, Germany and clinically relevant CoCr wear particles were generated using a six station pin-on-plate wear simulator. L929 fibroblast cells were cultured with 50µm3 of CoCr wear debris or composite ceramic particles at low to high volumes ranging from 500µm3–0.5µm3 per cell and the cyctotoxic effects of the particles were assessed over a period of 6 days using the ATP-Lite™ cell viability assay. The composite ceramic particles were bimodal in size (0.1–2µm & 30–100nm) and showed mild cytotoxic effects when compared with equivalent particle volumes (50µm3) of clinically relevant CoCr nano-particles (10–120nm). The CoCr nano-particles had significant cytotoxic effects from day 1, whereas the composite ceramic particles only showed cytotoxic effects at particle concentrations of 50 and 500µm3 after 6 days. The increased cytotoxicity of the clinically relevant CoCr nano-particles may have been attributed to the release of Co and Cr ions. This study demonstrated the potential cytotoxic effects of model ceramic particles at very high volume concentrations, but it is unlikely that such high particle volumes will be experienced routinely
The frictional torque of ceramic-on-ceramic bearings tended to increase with increasing the bearings size (32, 48, 56mm). However, the frictional torque was significantly lower than that measured on metal-on-metal bearings under well positioned and well lubricated conditions. Larger head size in total hip replacement theoretically provides increased range of motion and enhanced stability. However, there are potential clinical concerns regarding increased frictional torques with large diameter metal-on-metal bearings causing loosening of the acetabular cups and corrosion at the taper. The aim of this study was to determine the frictional torques of large diameter BIOLOX® delta ceramic-on-ceramic bearings.Summary Statement
Introduction
In vitro the introduction of microseparation and edge loading to hip simulator gait cycle has replicated clinically relevant wear rates and wear mechanisms in ceramic-on-ceramic bearings[1], and elevated the wear rates of MoM surface replacements (SR) to levels similar to those observed in retrievals[2]. The aim was to assess the wear of two different sized MoM total hip replacement bearings under steep cup inclination angles and adverse microseparation and edge loading conditions. Two tests were performed on the Leeds II hip joint simulator using two different size bearings (28mm and 36mm). Cups were mounted to provide inclination angles of 45 degrees (n=3) and 65 degrees (n=3). The first three million cycles were under standard gait conditions. Microseparation and edge loading conditions as described by Nevelos et al[1] were introduced to the gait cycle for the subsequent three million cycles. The lubricant was 25% new born calf serum. The mean wear rates and 95% confidence limits were determined and statistical analysis was performed using One Way ANOVA. Under standard gait conditions, when the cup inclination angle increased from 45 degrees to 65 degrees, the wear of size 28mm bearing significantly (p=0.004) increased by 2.7-fold, however, the larger bearings did not show any increase in wear (p=0.9). The introduction of microseparation conditions resulted in a significant (p=0.0001) increase in wear rates for both bearing sizes under both cup inclination angle conditions. Under microseparation conditions, the increase in cup inclination angle had no influence on the wear rate for both bearing sizes (Figure 1). With larger bearings, head-rim contact occurs at a steeper cup inclination angle providing an advantage over smaller bearings. The introduction of edge loading and microseparation conditions resulted in a significant increase in wear rates for both bearing sizes. The wear rates obtained in this study under combined increased cup inclination angle and microseparation were half of those obtained when SR MoM bearings were tested under similar adverse conditions[2]. This study shows the importance of prosthesis design and accurate surgical positioning of the head and acetabular cup in MoM THRs.