Abstract
Corrosion in modular taper connections of total joint replacement has become a hot topic in the orthopaedic community and failures of modular systems have been reported. The objective of the present study was to determine in vivo titanium ion levels following cementless total hip arthroplasty (THA) using a modular neck system.
A consecutive series of 173 patients who underwent cementless modular neck THA and a ceramic on polyethylene bearing was evaluated retrospectively. According to a standardized protocol, titanium ion measurements were performed on 67 patients using high-resolution inductively coupled plasma-mass spectrometry. Ion levels were compared to a control group comprising patients with non-modular titanium implants and to individuals without implants.
Although there was a higher range, modular-neck THA (unilateral THA: 3.0 μg/L (0.8–21.0); bilateral THA: 6.0 μg/L (2.0–20.0)) did not result in significant elevated titanium ion levels compared to non-modular THA (unilateral THA: 2.7 μg/L (1.1–7.0), p = 0.821; bilateral THA: 6.2 μg/L, (2.3–8.0), p = 0.638). In the modular-neck THA group, patients with bilateral implants had significantly higher titanium ion levels than patients with an unilateral implant (p < 0.001). Compared to healthy controls (0.9 μg/L (0.1–4.5)), both modular THA (unilateral: p = 0.029; bilateral p = 0.003) and non-modular THA (unilateral: p < 0.001; bilateral: p < 0.001) showed elevated titanium ion levels.
The data suggest that the present modular stem system does not result in elevated systemic titanium ion levels in the medium term when compared to non-modular stems. However, more outliner were seen in modular-neck THA. Further longitudinal studies are needed to evaluate the use of systemic titanium ion levels as an objective diagnostic tool to identify THA failure and to monitor patients following revision surgery.