Abstract
Introduction
In vitro findings (Bladed CL et al. ORS 2011 and J Biomed Mater Res B Appl Biomater, 2012) have suggested that UHMWPE wear particles containing vitamin-E (VE) may have reduced functional biologic activity and decreased osteolytic potential. Currently, there is no in vivo data determining the effects of wear debris from this new generation of implants. In this study we hypothesized that particles from VE-stabilized, radiation cross-linked UHMWPE (VE-UHMWPE) would cause reduced levels of osteolysis in a murine calvarial bone model when compared to virgin gamma irradiated cross-linked UHMWPE.
Methods
Study groups: 1). Radiation cross-linked VE-UHMWPE, 0.8% by weight, diffused after 100 kGy; 2). Radiation cross-linked virgin UHMWPE (virgin UHMWPE); 3). Shams. Particle generation and implantation: UHMWPE was sent to Bioengineering Solutions for particle generation. After IACUC approval, C57BL/6 mice (n = 12 for each group) received 3 mg of particulate debris overlying the calvarium and euthanized after 10 days. Micro-CT scans: Performed using an X-Tek-HMX-ST-225 with 70 kV voltage and 70 μA current. Topographical Grading Scale: Each calvarial bone was blindly scored with the following scale: 0 = No osteolysis, defined as intact bone; 1 = Minimal osteolysis, affecting 1/3 or less of the bone area; 2 = Moderate osteolysis, affecting at least 2/3 of the bone area; 3 = Severe osteolysis, defined as completely osteolytic bone. Histology H&E and TRAP staining was performed. Statistical Analysis: Inter-rater analysis was performed using Cohen's kappa analysis. Inter-rater coefficient >0.65 was considered as high inter-rater agreement. Comparison between groups was made using one-way ANOVA with post hoc Bonferroni correction for multiple comparisons. Correlations are reported as Spearman's rho. A p-value<0.05 was considered statistically significant.
Results
More than 83% of the VE-UHMWPE and more than 85% of the virgin UHMWPE particles measured less than 1 μm in mean particle size. There was a statistically significant greater level of osteolysis visualized on the topographical grading scale in calvaria implanted with virgin UHMWPE wear particles. The micro-CT findings were confirmed histologically (Fig. 1). A greater amount of inflammatory tissue overlaying the calvaria was observed in the virgin UHMWPE group when compared to both shams and VE-UHMWPE groups. Post hoc analysis revealed significant difference between VE-UHMWPE and virgin UHMWPE for the topographical osteolysis grading score (p = 0.002) but no difference in osteoclast count (p = 0.293).
Discussion/Conclusion
This is the first in vivo study reporting the effects of clinically-relevant UHMWPE particles generated from a VE-UHMWPE implant that is in current clinical use. These results suggest that VE-UHMWPE particles have reduced osteolysis potential in vivo when compared to virgin, highly cross-linked UHMWPE in a murine calvarial bone model.