High failure rates with a large diameter hybrid metal on metal total hip replacement: clinical, radiological and retrieval analysis

British Orthopaedic Association/Irish Orthopaedic Association Annual Congress (BOA/IOA)



Abstract

This study reports the mid-term results of a large bearing hybrid metal on metal total hip replacement (MOMHTHR) in 199 hips (185 patients) with mean follow up of 62 months. Clinical, radiological, metal ion and retrieval analysis were performed.

Seventeen patients (8.6%) had undergone revision, and a further fourteen are awaiting surgery (defined in combination as failures). Twenty one (68%) failures were females. All revisions and ten (71%) awaiting revision were symptomatic. Twenty four failures (86%) showed progressive radiological changes.

Fourteen revision cases showed evidence of adverse reactions to metal debris (ARMD). The failure cohort had significantly higher whole blood cobalt ion levels (p=0.001), but no significant difference in cup size (p=0.77), inclination (p=0.38) or cup version (p=0.12) compared to the non revised cohort. Female gender was associated with increased risk of failure (p=0.04). Multifactorial analysis demonstrated isolated raised Co levels in the absence of symptoms or XR changes were not predictive of failure (p=0.675). However the presence of pain (p<0.001) and XR changes (p<0.001) in isolation were significant predictors of failure. Wear analysis (n=5) demonstrated increased wear at the trunnion/head interface (mean out of roundness measurements 34.5 microns (normal range 8–10 microns) with normal wear levels at the articulating surfaces. Macroscopically corrosion was evident at the proximal and distal stem surfaces. Cumulative survival rate, with revision for any reason was 92.4% (95%CI: 87.4–95.4) at 5 years. Including those awaiting surgery, the revision rate would be 15.1% with 89.6% (95% CI: 83.9–93.4). Cumulative survival at 5 years.

This MOMHTHR series has demonstrated unacceptable high failure rates with evidence of high wear at the head/trunnion interface and passive corrosion to the stem surface. Female gender was an independent risk factor of failure. Metal ion levels remain a useful aspect of the investigation work up but in isolation are not predictive of failure.