Abstract
The growing number of non-union fractures in an aging population has increased the clinical demand for tissue-engineered bone. Electrical stimulation (ES) has been described as a promising strategy for bone regeneration treatments in several clinical studies. However the underlying mechanism by which ES augments bone formation is still poorly understood and its use in bone tissue engineering (BTE) strategies is currently underexplored. Additive manufacturing (AM) technologies (Fused Deposition Modeling/3D Printing) have been widely used in BTE due to their ability to fabricate scaffolds with a high control over their structural and mechanical properties in a reproducible and scalable manner. Thus, in this work, we combined AM methods with conductive biomaterials and ES to enhance the osteogenic differentiation of human bone marrow-derived mesenchymal stem/stromal cells (hBMSCs) envisaging improved BTE strategies.
First, we started by developing AM-based electro-bioreactor devices containing medical-grade electrodes (stainless steel and Ti6Al4V) to apply ES to monolayer 2D cultures and 3D cell-seeded scaffolds. Computer modeling(Finite Element Analysis-FEA) was employed to predict the magnitude/distribution of electrical fields within the ES devices and along the different conductive scaffolds. Prior to scaffold culture, 5 different ES protocols were tested in terms of their ability to promote hBMSCs proliferation and osteogenic differentiation in 2D cultures. The best performance ES protocol was then used in two different AM-based BTE strategies: 1) Two different conductive scaffolds (conductive poly lactic acid (PLA) and titanium) were seeded with hBMSCs and cultured for 21 days under osteogenic medium conditions with and without ES and their biological performance was evaluated in comparison to non-conductive standard PLA scaffolds; 2) Different PEDOT:PSS-based coating solutions were screened to obtain PEDOT:PSS/Gelatin-coated 3D polycaprolactone (PCL) scaffolds with a high(11 S.cm-1) and stable electroconductivity. When cultured under ES, PEDOT:PSS/Gelatin-PCL scaffolds enhanced significantly hBMSCs osteogenic differentiation and mineralization(calcium deposition), highlighting their potential for BTE applications.
Acknowledgements: Funding received from FCT through projects InSilico4OCReg (PTDC/EME-SIS/0838/2021), OptiBioScaffold (PTDC/EME-SIS/4446/2020) and BioMaterARISES (EXPL/CTM-CTM/0995/2021), and to the institutions iBB (UIDB/04565/2020), CDRSP (UIDB/04044/2020) and Associate Laboratory i4HB (LA/P/0140/2020).