Antibacterial activity of coatings based on metal and metal oxide nanoparticles (NPs) often depends on materials and biotic targets resulting in a material-specific killing activity of selected Gram-positive and Gram-negative bacteria, including drug-resistant strains. In this perspective, the NPs loading amount, the relative elemental concentration inside the nanogranular building blocks and the deposition method are of paramount importance when the goal is to widen the antimicrobial spectrum, but at the same time to avoid high levels of metal content to limit undesired toxic effects. Aim of the present study was evaluation of the antimicrobial properties of two multielement nanogranular coatings composed of Titanium-Silver and Copper and of Magnesium-Silver and Copper.
Method
Ti-Ag-Cu and Mg-Ag-Cu NPs were deposited on circular cover glasses (VWR) by Supersonic Cluster Beam Deposition. Biofilm-producer strains of Staphylococcus aureus (methicillin susceptible and resistant), Staphylococcus epidermidis (methicillin susceptible and resistant), Escherichia coli (fully susceptible and producer of extended spectrum beta lactamases), and Pseudomonas aeruginosa (susceptible and multidrug-resistant) were selected. The abilities of the selected strains to adhere, colonize and produce biofilm on the discs coated with Ti-Ag-Cu or Mg-Ag-Cu NPs were compared to uncoated circular cover glasses which were used as growth control. Cytotoxicity was also evaluated in order to assess the biocompatibility of the newly synthesized NPs.
Results
In comparison to uncoated controls, both coatings showed significant anti-adhesive properties against S. aureus, S. epidermidis, and E. coli. Reduction in adhesion to Mg-Ag-Cu coated discs was observed also for P. aeruginosa isolates, although differences vs uncoated controls did not reach statistical significance. Biofilm formation was reduced on discs coated with Mg-Ag-Cu compared to Ti-Ag-Cu and, again, coatings had a milder effect on P. aeruginosa, probably due to its exceptional capability of attachment and matrix production. These results were confirmed by the evaluation of bacterial colonization on nanoparticles-coated discs by means of confocal laser scanning microscopy. A viability of 95.8% and 89.4% of cells cultured in the presence of Ti-Ag-Cu and Mg-Ag-Cu discs, respectively, when compared to negative controls was observed, thus excluding cytotoxic effects on eukaryotic cells.
Conclusions
The newly synthesized Ti-Ag-Cu and Mg-Ag-Cu coatings are able to limit bacterial adhesion colonization and biofilm production, thus highlighting the safe use of multi-element families of NPs as new strategies against bacterial attachment to the surface of biomedical implants. However, further studies addressing activity against P. aeruginosa and including a wide number of isolates are warranted.