Abstract
Introduction and Objective
Bone is a tissue which continually regenerates and also having the ability to heal after injuries however, healing of large defects requires intensive surgical treatment. Bioactive glasses are unique materials that can be utilized in both bone and skin regeneration and repair. They are degradable in physiological fluids and have osteoconductive, osteoinductive and osteostimulative properties. Osteoinductive growth factors such as Bone Morphogenetic Proteins (BMP), Vascular Endothelial Growth Factor (VEGF), Epidermal Growth Factor (EGF), Transforming Growth Factor (TGF) are well known to stimulate new bone formation and regeneration. Unfortunately, the synthesis of these factors is not cost- effective and, the broad application of growth factors is limited by their poor stability in the scaffolds. Instead, it is wise to incorporate osteoinductive nanomaterials such as graphene nanoplatelets into the structures of synthetic scaffolds. In this study, borate-based 13-93B3 bioactive glass scaffolds were prepared by polymer foam replication method and they were coated with graphene-containing poly (ε-caprolactone) layer to support the bone repair and regeneration.
Materials and Methods
Effects of graphene concentration (1, 3, 5, 10 wt%) on the healing of rat segmental femur defects were investigated in vivo using male Sprague–Dawley rats. Fabricated porous bioactive glass scaffolds were coated by graphene- containing polycaprolactone solution using dip coating method. The prepared 0, 1, 3, 5 and 10 wt% graphene nanoparticle-containing PCL-coated composite scaffolds were designated as BG, 1G-P-BG, 3G-P-BG, 5G-P-BG and 10G-P-BG, for each group (n: 4) respectively. Histopathological and immunohistochemical (bone morphogenetic protein, BMP-2; smooth muscle actin, SMA and alkaline phosphatase, ALP) examinations were made after 4 and 8 weeks of implantation.
Results
Results showed that after 8-weeks of implantation both cartilage and bone formation were observed in all animal groups. After 4 and 8 weeks of implantation the both osteoblast and osteoclast numbers were significantly higher in the group 4 compared to the control group. Bone formation was significant starting from 1 wt% graphene-coated bioactive glass implanted group and highest amount of bone formation was obtained in group containing 10 wt% graphene (p<0.001). Newly formed vessels expressed this marker and increased vascularization was observed in 8- weeks period compared to the 4-weeks period. In addition, an increase in new vessel formation were observed in graphene-coated scaffold implanted groups compared to the control group. While cartilage tissue was observed in control group, bone formation percentages were significant in graphene-coated scaffold implanted groups. Highest amount of bone formation occurred in group 4 (10 % wt G-C).
Conclusions
Additionally, the presence of graphene nanoplatelets enhanced the BMP-2, SMA and ALP levels compared to the bare bioactive glass scaffolds. It was concluded that pristine graphene-coated bioactive glass scaffolds improve osteointegration and bone formation in rat femur defect when compared to bare bioglass scaffolds.