Abstract
Adherent cells are known to respond to physical characteristics of their surrounding microenvironment, adapting their cytoskeleton and initiating signaling cascades specific to the type of cue encountered. Scaffolds mimicking native biophysical cues have proven to differentiate stem cells towards tissue-specific lineages and to maintain the phenotype of somatic cells for longer periods of culture time. Although the characteristic anisotropy of tendon tissue is commonly replicated in scaffolds, relevant physical cues such as tendon rigidity or mechanical loading are often neglected. The objective of this study is to use tendons' main extracellular matrix component, collagen type I, to create scaffolds with an anisotropic surface topography and controlled rigidity, in an effort to engineer functional tendon tissue equivalents, with native organization and strength.
Porcine collagen type I in solution was treated with one of the following cross-linkers: glutaraldehyde, genipin or 4-arm polyethylene glycol (4SP). The resulting mixture was poured on micro-grooved (2×2×2 μm) or planar polydimethylsiloxane (PDMS) molds and dried in a laminar flow hood to obtain 5 mg/ml collagen films. Surface topography and elastic modulus of the final scaffolds were analyzed using SEM/AFM and rheometry, respectively. Human tendon cells were isolated from adult tendon tissue and cultured on micro-grooved/planar scaffolds for 4, 7 and 10 days. Cell morphology, collagen III and tenascin C expression were analyzed by immunocytochemistry.
Among the different cross-linkers used, only the treatment with 4SP resulted in scaffolds with a recognizable micro-grooved surface topography. Precise control over the micro-grooved topography and the rigidity of the scaffolds was achieved by cross-linking the collagen with varying concentrations of 4SP at low pH and temperature. The elastic modulus of the scaffolds cross-linked with the highest concentration of 4SP matched the physiological values reported in developing tendons (∼15 kPa). Around eighty percent of the human tendon cells cultured on the cross-linked collagen films aligned in the direction of the anisotropy for 10 days in culture. At 4 days, tenoyctes cultured on micro-grooved substrates presented a significant higher nuclei aspect ratio than tenocytes cultured on planar substrates for all the 4SP concentrations. Synthesis, deposition and alignment of collagen III and tenascin C, two important tenogenic markers, were up regulated selectively in the rigid micro-grooved scaffolds after 7 days in culture. These results highlight the synergistic effect of matrix rigidity and cell alignment on tenogenic cell lineage commitment.
Collectively, this study provides new insights into how collagen can be modulated to create scaffolds with precise imprinted topographies and controlled rigidities. Gene expression analysis and a replicate study with hBMSCs will be carried out to support the first results and to further identify the optimal biophysical conditions for tenogenic cell lineage commitment. This potentially leads to the design of smart implants that not only restore immediate tendon functionality but also provide microscopic cues that drive cellular synthesis of organized tissue-specific matrix.