Abstract
A novel injectable hydrogel based on DNA and silicate nanodisks was fabricated and optimized to obtain a suitable drug delivery platform for biomedical applications. Precisely, the hydrogel was designed by combining two different type of networks: a first network (type A) made of interconnections between neighboring DNA strands and a second one (type B) consisting of electrostatic interactions between the silicate nanodisks and the DNA backbone. The silicate nanodisks were introduced to increase the viscosity of the DNA physical hydrogel and improve their shear-thinning properties. Additionally, the silicate nanodisks were selected to modulate the release capability of the designed network.
DNA 4% solutions were heated at 90°C for 45 seconds and cooled down at 37°C degree for two hours. In the second step, the silicate nanodisks suspension in water at different concentrations (0.1 up to 0.5%) were then mixed with the pre-gel DNA hydrogels to obtain the nanocomposite hydrogels. Rheological studies were carried out to investigate the shear thinning properties of the hydrogels. Additionally, the hydrogels were characterized by scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR), and X-ray photoelectron microscopy. The hydrogels were loaded with the osteoinductive drug dexamethasone and its release was tested in vitro in phosphate buffer pH 7.4. The drug activity upon release was tested evaluating the osteogenic differentiation of human adipose derived stem cells (hASCs) in vitro through analysis of main osteogenic markers and quantification of alkaline phosphatase activity and calcium deposition. Finally, the hydrogels were tested in vivo and injected into cranial defects in rats to assess their biocompatibility and bone regeneration potential.
The inclusion of the silicate nanodisks increased the viscosity of the hydrogels and the best results were obtained with the highest concentration of the nanoclay (0.5%). The hydrogels possessed shear-thinning properties as demonstrated by cyclic strain sweep tests and were able to recover their original storage modulus G' upon removal of strain. Such improvement in the injectable properties of the formulated hydrogels was mainly attributed to the formation of electrostatic interactions between the silicate nanodisks and the phosphate groups of the DNA backbone as confirmed by XPS analysis of the O, N, and P spectra. Additionally, laponite was able to sustain the release of the osteoinductive drug dexamethasone which was instead completely released from the DNA-based hydrogels after a week. The drug after being released was still active and promoted the osteogenic differentiation of hASCs as confirmed by ALP expression and expression of main osteogenic markers including ALP and COLA1. Finally, the gels proved to be biocompatible in vivo when injected into cranial defects and promoted bone formation at the periphery of the defect after a month post-treatment.
A novel injectable shear-thinning DNA-based hydrogel was characterized and tested for its drug delivery properties. The hydrogel can promote the sustain release of a small molecule like dexamethasone and be biocompatible in vitro and in vivo. Due to these promising findings, the designed system could find also applicability for the delivery of growth factors or other therapeutic molecules.
