Abstract
Polymethylmethacetate (PMMA) is a bone cement used in over 725,000 primary hip arthroplasties in 2018. Cement integrity is affected by external factors, including temperature, mixing technique and moisture uptake, which can influence cement microstructure. Changes in the cement microstructure may ultimately threaten the survivorship of the implant.
The introduction of enhanced recovery and various local anaesthetic infiltration techniques have been adopted in an attempt to facilitate early mobilisation and reduce length of stay. Our study aims to investigate if the mechanical properties of PMMA are altered with exposure to Ropivacaine LA.
Cements were cured in three separate states (air, serum and serum with LA) and the mechanical properties tested at 24 hours and 28 days. Using Refobacin bone cement provided by ZimmerBIOMET, cylindrical molds (12×6mm) were constructed with a split-mold. The LA used was 2mg/ml Ropivacaine hydrochloride solution. Using pilot data, this study was powered to 80% and a sample size of 10 per group (n=60) was calculated.
Cement samples were subjected to compressive loading using a universal testing apparatus (Zwick/Roell). Yield-strength and modulus values were extracted from the respective stress versus strain curves. Significant differences were determined by one-way anova for each time point, and Bonferroni post-hoc testing to determine significance between actual groups.
At 24-hours there were no significant differences in strength or modulus between groups. At 28-day strength and modulus increased in all groups. Compared to the air group, both serum and LA groups show a significant decrease in compressive strength. The modulus for the LA group is significantly less stiff compared to the air group.
The results suggest that the initial exposure to LA has a significant impact on the physical properties of the PMMA. We propose increased awareness of the potential effects this may have on the longevity and survivorship of cemented implants.