Abstract
Background
One of the potential complications of polyethylene liner (PL) is its dissociation from the metal shell. This is a rare but catastrophic complication of total hip replacement (THR).
Objective
was to analyze the retrieved dissociated components (PL and shell) (Depuy Pinnacle, Warsaw, IN, USA) to evaluate the mechanism of failure. All these components were dissociated within four years of implantation.
Methods
Components were retrieved from three different centers in Canada over the period from January 2011 to October 2016. The analysis was done at the Orthopaedic Innovation Centre (OIC) in Winnipeg Canada. Nine PLs were retrieved at the time of revision THR. Assessment using optical and scanning electron microscopies at magnification between 25× and 150× was performed. The following questions were asked: 1) were the liners correctly seated at the primary surgery? 2) Are there signs of impingement present which could have caused the liner to become dissociated? 3) Does the wear pattern indicate that the liner was failing prior to dissociation?
Results
All PLs dissociated in the inferior direction. Five PL were believed to have been seated properly at the time of indexed surgery. All PL displayed signs of post dissociation impingement. Only 1 PL had fractured resulting in failure prior to dissociation. Other PL showed signs of wear, however none of them reached thinness that would be a cause for concern. Eight PLs demonstrated shearing of the anti rotation tabs. Assessment of the anti rotation tabs revealed that a couple had sheared off suddenly while remaining anti rotation tabs sheared off in progressive fatigue resulting in the failure of the locking mechanism.
Conclusions
Retrieval analysis was useful in identifying common patterns of failure such as anti-rotation tab damage. This was suggestive that the locking mechanism of the acetabular components has probably failed in 8 out of 9 of the retrieved liners.