Abstract
Introduction
Despite the positive outcomes in shoulder joint replacements in the last two decades, polyethylene wear debris in metal-on-polyethylene artificial shoulder joints is well-known as a limitation in the long-term survival of shoulder arthroplasties systems. Consequently, there is an interest in the use of novel materials as an alternative to hard bearing surfaces such as pyrolytic carbon layer (PyroCarbon).
Materials and Methods
In the present study, the unique Newcastle Shoulder Wear Simulator was used (Smith et al., 2015; Smith et al., 2016) to evaluate the wear behavior of four commercially available PyroCarbon humeral heads 43 mm diameter, articulating against conventional ultra-high molecular weight polyethylene (UHMWPE) glenoid inserts with a radius of curvature of 17.5 mm to form an anatomic total shoulder arthroplasty.
A physiological combined cycled “Repeat-motion-load” (RML) (Ramirez-Martinez et al., 2019) obtained from the typical activities of daily life of patients with shoulder implants was applied as a simulator input. A fifth sample of the same size and design was used as a soak control and subjected to dynamic loading without motion during the wear test. The mean volumetric wear rate of PyroCarbon-on-polyethylene was evaluated over 5 million cycles gravimetrically and calculated on the basis of linear regression, as well as the change in surface roughness (Sa) of the components using a non-contacting white light profilometer throughout the test.
Results
The gravimetric analysis showed a mean volumetric wear rate and standard deviation of 19.3±9.5 mm3/million cycles for the UHMWPE glenoid inserts, whereas PyroCarbon humeral head counterparts did not exhibit a loss in mass throughout the test. The roughness values of the UHMWPE glenoid inserts decreased (P < .001), changing from 296±28 nm to 32±8 nm at the end of the test. In contrast, the PyroCarbon humeral heads did not show a significant change (P = .855) over the 5 million cycles; remained in the same range (21±2 nm to 20±10 nm) with no evidence of wear damage on the surface.
Conclusions
This is the first in-vitro shoulder simulator study of a PyroCarbon on UHMWPE articulation. Wear rates were similar to that found to well-proven metal on UHMWPE shoulder arthroplasties. While it was interesting to see that the PyroCarbon did not roughen over the test duration, the lack of an appreciable reduction in wear of the UHMWPE component when articulated with an expensive and complex to manufacture PyroCarbon component likely means there is little clinical cost-benefit in the use of a PyroCarbon on UHMWPE shoulder implant.
Declaration of competing interest
Prof. Ian A. Trail received some royalties and research support from Wright Medical Group N.V. None of the other authors, their immediate families, and any research foundation with which they are affiliated did not receive any financial payments or other benefits from any commercial entity related to the subject of this article.
For any figures or tables, please contact authors directly.