Abstract
Two big problems exist with the all polyethylene cemented tibial component; the polyethylene and the cement. The polyethylene is too weak and flexible to bear high tibial load, so it deforms and loosens. The interface stresses are too high when two flexible structures are poorly bonded and heavily loaded.
Modularity between the polyethylene tibial component and the metal-backed tray was introduced in the mid-80's for versatility and to facilitate screw fixation for cementless implants. These designs allow exchange of various polyethylene thicknesses, and aids the addition of stems and wedges. Other advantages include the reduction of inventory, and the potential for isolated tibial polyethylene exchanges as a simpler revision procedure. Several studies have documented the high failure rate of isolated polyethylene exchange procedures, because technical problems related to the original components are left uncorrected. However, revision for wear is the simplest revision ever!
Since the late 1980's the phenomena of polyethylene wear and osteolysis have been observed much more frequently when compared with earlier eras. The reasons for this increased prevalence of synovitis, progressive osteolysis, and severe polyethylene wear remain unclear. There is some association with the widespread use of both cementless and cemented modular tibial designs. Improved polyethylene attachment is the answer even if a screw, a wire, or a pin is needed. Do not abandon the modular tibia.