Abstract
The concept of decellularised xenografts as a basis for anterior cruciate ligament (ACL) reconstruction was introduced to overcome limitations in alternative graft sources such as substantial remodelling delaying recovery and donor site morbidity. This study aimed to measure the biomechanical properties of decellularised porcine super flexor tendon (pSFT) processed to create ACL grafts of varying diameters, with a view to facilitating production of stratified ‘off the shelf’ products with specified functional properties for use in ACL reconstructive surgery.
Decellularisation was carried out using a previously established procedure, including antibiotic washes, low concentration detergent (0.1% sodium dodecyl sulphate) washes and nuclease treatments. Decellularised pSFTs were prepared to create double-bundle grafts of 7, 8 and 9mm diameter (n=6 in each group). Femoral and tibial fixations were simulated utilising Arthrex suspension devices (Tightrope®) and interference screws in bovine bone respectively.
Dynamic stiffness and creep were measured under cyclic loading between 50–250N for 1000 cycles at 1Hz. This was followed by ramp to failure at 200mm/min from which linear stiffness and load at failure were measured. Data were analysed using either 1- or 2-way ANOVA as appropriate with Tukey post-hoc analysis (p<0.05).
Significant differences were found between all groups for dynamic stiffness and between 7 & 9mm and 8 & 9mm groups for dynamic creep. Significant differences were also found between 7, 8 & 9mm groups for linear stiffness (167.8±4.9, 186.9±16.6 & 216.3±12.4N/mm respectively), but no significant differences were found between groups for load at failure (531.5±58.9, 604.1±183.3 & 627.9±72.4N respectively).
This study demonstrated that decellularised pSFTs possess comparable biomechanical properties to other ACL graft options (autografts and allografts). Furthermore, grafts can be stratified by their diameter to provide varying biomechanical profiles depending on the anatomy and individual needs of the recipient.