Abstract
We report a case of fatal heart failure caused by cobalt intoxication after revision THR in the patient who successfully underwent re-revision THR. 53-year old male presented to emergency room in our hospital with progressive shortness of breath. Symptom was started about 6 months ago so he visited local hospital. He worked up for worsening dyspnea. Simple chest radiograph and enhanced heart MRI study were performed and they showed bilateral pericardial and pleural effusion. There was no evidence of ischemic change. Transthoracic echocardiogram showed the evidence of heart failure, left ventricular ejection fraction(EF) was 40%. He was admitted at local hospital and started on vasopressors but urine output was decreased and follow-up echocardiogram showed a 25% of EF. Patient recommended heart transplantation and transferred our hospital emergency room. He underwent sequential bilateral total hip arthroplasties using CoP bearing surfaces. At 12 years postoperatively, he presented to the other hospital with acute onset of left hip pain. He was diagnosed ceramic head fracture on his left hip. Head and liner change revision surgery was performed using Cobalt-Chrome alloy 28mm metal head and Protruded cross-linked polyethylene liners. In our hospital, the patient admitted cardiovascular department of internal medicine. Patient complained nonspecific fatigue and general weakness but had no other symptoms such as visual and hearing loss, cognitive dysfuction. During work-up, patient presented progressive left hip pain and complaint of discomfort for the mass on the left groin. He also complained Left leg weakness and numbness. Simple radiograph and enhanced CT study was done. Simple radiograph image shows radiodense area around the hip joint and radiologist suspected heterotopic ossification. The cardiovascular department consulted orthopedic department. In the image findings showed huge mass combined hemorrhagic component lining acetabular component extending psoas compartment and eccentric wear on cobalt-chrome alloy metal head. Also highly radiodense material was seen around neck inferor portion and severly deformed metal head was seen. It was highly suspected that metal related granuloma, which means severe metallosis. Performed heavy metals screen, cobalt levels were 397,800 μg/Land chrome levels were 236,000 μg/L suggesting cobalt toxicity. Hip joint aspiration was done for decompression as radiologic intervention and EDTA (ethylenediamine tetraacetate) chelation therapy started immediately. After 10 cycle chelating therapy, metal level was lowered cobalt levels by 255.2μg/L and chrome levels by 39.5 μg/L. When hospital day after 134, Medical condition of the patient was getting improved, we underwent revision surgery using ceramic on ceramic bearing surface. The patient discharged postoperative 79 days. Final heavy metals screen results were 27.79μg/L on cobalt and 22.17μg/L on chrome. Although there were also reported a good clinical result of revision surgery using MoP bearing, and some surgeons reluctant to use CoC articulation because of concerns about re-fracture of ceramic. But take into account like this devastating complication after cobalt-chrome wear caused by remained ceramic particles, we should carefully select which bearing is safer.
