Osteolysis secondary to ultra-high molecular weight polyethylene (UHMWPE) wear is a leading cause of late-term implant failure via aseptic loosening in patients treated with total hip arthroplasty (THA). Radiation crosslinking of UHMWPE has been shown to decrease wear. However, the resulting polymer (crosslinked-PE) has a high free radical content. Two different methods that have been used to reduce the remaining free radicals are mechanical annealing and chemical stabilization using Vitamin E, a free radical scavenger.
The primary purpose of the current study was to evaluate and compare the wear properties of vitamin E-doped crosslinked-PE (VEPE) and one formulation of mechanically annealed crosslinked-PE using radiostereometric analysis (RSA) in patients five years after primary THA. We also sought to understand the association between polyethylene wear and patient-reported outcome measures (PROMs).
Three-hundred and five patients from six international centers were enrolled. Seventy-six percent were treated with highly-crosslinked (95 kGy) VEPE liners, and the rest received moderately-crosslinked (50 kGy) (ModXL), mechanically annealed liners. Data was collected prospectively at one-, two-, and five-year intervals.
At the 5-year follow-up, proximal femoral head penetration into the VEPE liners (median = 0.05mm (range, −0.03–1.20)) was significantly lower than the penetration into the ModXL liners (median = 0.15mm (range, −0.22–1.04)) (p<0.001). In the VEPE cohort the median proximal penetration did not increase from one- to five-year follow-up (p=0.209). In contrast, there was a significant increase in femoral head penetration for the ModXL group (p<0.001) during that same time. Multivariable regression showed that the only variable predictive of increased wear was ModXL liner type (B=0.12, p<0.001). There were no differences in PROMs between the liner groups, and there was no correlation between polyethylene wear and PROMs for the cohort as a whole.
The current study is the largest analysis of polyethylene wear at five-year follow-up using the RSA technique. We observed similar bedding in through the two-year interval between the two liner types, however, there was significantly more wear in the ModXL cohort at five-years. Currently, the wear rates for both liner groups are below the osteolysis threshold and have not led to any implant failures via aseptic loosening. Continued follow-up will provide a better understanding of the association between wear rate and clinical outcomes.