Abstract
Polyethylene wear is the most important risk factor affecting the durability of total knee arthroplasty. We developed a new method of measuring wear of the tibial polyethylene insert in total knee arthroplasty (TKA) on standard standing radiographs.
Methods: We developed a new method of measuring the shortest distance between the femoral component and the tibial metal tray taking its 3-D position into consideration. The accuracy of the method was examined in 3 conditions. An in vitro examintion measured the thickness of the polyethylene on radiographs of a new PFC prosthesis set on a table. The radiographs were taken from various directions. An in vivo examination measured the polyethylene thickness on patient discharge radiographs of 78 knees. These measurements were compared with known thicknesses of the used inserts. In the third study, wear of the tibial polyethylene insert was measured retrospectively in a series of 84 PFC TKAs with follow-up of 2 to 10 years (6.6 years on average).
Results: The average measurement error was 0.05 mm (SD 0.09 mm) in the in vitro study and 0.14 mm (SD 0.17 mm) in the in vivo study using discharge radiographs. In the series of 84 PFC TKAs, impending failure occurred in 7 knees, 4 of which were revised. Radiographically measured wear of the tibial insert was significantly greater in these failed TKAs than in the other TKAs. The radiographic measurements were well correlated with 3-D measurements of 4 retrieved inserts.
Discussion: Although the radiographic measurement of the tibial insert in TKA was less accurate than that of the socket in THA, it is useful enough to identify TKAs at risk of failure. When the radiographic wear exceeded 1mm, there was a significantly increased probability of impending failure or need for revision.
The abstracts were prepared by Nico Verdonschot. Correspondence should be addressed to him at Orthopaedic Research Laboratory, University Medical Centre, PO Box 9101, 6500 HB Nijmegen, The Netherlands.