ACETABULAR SHELLS WITH SCREWS INCREASE THE RISK OF OSTEOLYSIS FOLLOWING THR: A CT-BASED ANALYSIS

Abstract

Pelvic osteolysis secondary to polyethylene wear is a major complication following THR. Identification of implant specific characteristics associated with osteolysis is essential. The purpose of this study is to compare incidence of CT scan identifiable osteolysis in 2 groups of young, active patients following THR; one with multi-holed acetabular shells with screws, one with cups without screw holes.

Between 1990–1993, 77 patients (85 hips) underwent THR with a cementless titanium, multi-holed shell with screws, modular, compression molded polyethylene and an uncemented titanium femoral stem. Average follow-up: 9 years, average age at surgery: 51 years. Between 1984–1987, 163 patients (183 hips) underwent THR with a cementless cobalt-chrome, solid shell, modular, heat-pressed polyeth-ylene liner and uncemented cobalt-chrome femoral stem. Average follow-up: 16 years, average age at operation: 52 years. All polyethylene was irradiated in air. At most recent follow-up, CT scans with metal suppression software was obtained to evaluate incidence of pelvic osteolysis. Patients classified: Group 1-no osteolysis, Group 2-cavitary osteolysis, Group 3-segmental osteolysis.

Patients with titanium, multi-holed shells had: Group 1-50.0%, Group 2-38.7%, and Group 3-11.3%. Patients with cobalt-chrome, solid shells had: Group 1-59.3%, Group 2-33.3% and Group 3-7.4%.

Although the patients with solid cups had much longer follow-up, less secure capture mechanism, less congruency between polyethylene and shell, and heat-pressed polyethylene, the incidence and extent of pelvic osteolysis was less than in the patients with multi-holed shell with screws. The presence of 6.5 mm cancellous screws is a serious independent risk factor for pelvic osteolysis following THR.